Zoom Logo

Characterization Webinar - Shared screen with speaker view
Ghadendra Bhandari
02:36:11
Good Morning to everybody from WV.
Jessica
02:36:29
Good morning all, from Valparaiso, IN!
kirshar
02:36:46
Good Morning all, from Potsdam,NY
Yordy Fonseca
02:37:09
Good Morning all, from Rio de Janeiro, Brazil
lacns
02:37:13
Good morning from Baton Rouge, LA
Koray Sekeroglu
02:37:25
good morning from St. Paul, Minnesota
sardela
02:37:28
you need to unmute me
Julio Soares
02:37:38
Good morning
Whitney
02:37:38
Hey!!! Richmond, VA here
Sohaila Aboutaleb
02:37:42
good morning from urbana, IL
Tori Cox
02:37:43
Good morning from Ames, IA!
Steve H
02:37:50
greetings from Poquoson, VA
lian xiujun
02:37:51
Good morning from Florida!
dadhikar
02:38:01
Good Morning everyone, from the University at Buffalo, Buffalo NY
Marcell
02:38:03
Good morning from Amherst -NY -USA
sardela
02:38:04
No
Shiv Prakash Singh
02:38:05
We can hear you!
kuilin
02:38:07
Good morning from Urbana, IL
Md Abdul Halim
02:38:10
good morning from Texas
Alan
02:38:21
Good morning rom NY
FOM Networks
02:38:21
Hello from FOM Networks, Chicago. www.fomnetworks.com
Robert Kennedy
02:38:23
Morning from Evanston, IL!
Isabella
02:38:28
Hello from Cambridge, MA!
Joe
02:38:33
Good Morning from Rochester,NY
winston peloso
02:38:35
Good morning from Princeton NJ!
sardela
02:38:36
I am still muted
bram kuijer
02:38:39
Hello from Dartmouth College
Bikram
02:38:40
good morning All
Md Farhadul Haque
02:38:41
good morning
sidd
02:38:47
Hi from Lafayette, Indiana
Mahmut
02:41:44
Good morning All
Sung Yeom
02:46:20
It seems room is full so other people cannot join the webinar.
Jeffrey Shallenberger
02:46:59
yes, we thought we had increased to 1000 but somthing went wrong. we are recording and will send out afterwards.
felix
02:47:20
Will you send out previous recordings as well please?
FOM Networks
02:49:43
@Jeff, are you posting the recordings on the website or sending out to registered emails only?
Jeffrey Shallenberger
02:50:46
yes. SIMS and XRD will be posted on our YouTube channel https://www.youtube.com/pennstatemri
felix
02:51:01
Great! Thanks!
Qingyi Zhou
02:51:25
Thanks a lot! Subscribed.
Iman Abdallah
02:57:21
Thanks!
Gourab Bhaskar
03:03:49
What do you mean by peak areas (FWHM)?If not then how to calculate it?
Nana Adoo
03:04:18
full wave half max
Gourab Bhaskar
03:04:41
ok (fulll width btw)
Mark Levenstein
03:04:59
Full width* half maxiumum
Mark Levenstein
03:05:11
maximum
Nana Adoo
03:05:21
width
Qvas
03:07:20
What software does he use for analysis?
Metin
03:07:42
Looks like MDI Jade
Marcell
03:08:40
/r
Quinn Leonard
03:11:35
Well, at least you are not an outlier, Jerry!
Derrick J Butler
03:18:16
Can the X-ray radiation alter the material such that the material changes between start to finish of the scan, potentially modifying the spectrum? If so, do you have an example?
Timothy Spila
03:20:33
Can you comment on getting material concentration from RLM measurements?
Tong, Xin
03:22:37
This might be a naive question. But could you say that a fine powder form sample can be representative for the entire sample? Or do we need to test on multiple spots to get comprehensive results? Thank you very much.
shruti
03:24:24
What is the smallest volume fraction in a composite that can be detected in a regular theta-2theta scan?
adam w
03:24:31
With nanoscale materials with broad peaks, is there a method to account for broad peaks which blend in with the baseline when analyzing data?
ahall
03:28:25
thank for doing this weinar!
PJakubcova
03:28:55
thank you
Weiling Dong
03:28:59
Great webinar! Thanks!
ahall
03:29:01
Thank you doing this webinar(meant to say)
Shiv Prakash Singh
03:29:27
Is it possible to use this technique for liquid samples in simple way
Lei Wang
03:29:35
thanks
yang wu
03:29:44
Thanks
dadhikar
03:30:02
Very useful Webinar! Thanks for organizing it
Whitney
03:30:09
Great webinar, very interested in a part 2 from you! Thank you
Weiling Dong
03:30:28
For XRR, how to deal with rough interface, and intermixing/inter-diffusion interface?
Ishani Khurana
03:30:33
thanks
Md Abdul Halim
03:30:33
can we do XRD for organic entity sandwiched between metal oxide layers in nanocomposites?
Martin Lonsky
03:30:49
Thank you for the very instructive presentation, Mauro!
Quinn Leonard
03:31:06
Excellent talk.
Metin
03:31:13
Is it possible to measure the density of polymer ceramic composite thin films by XRR?
Jessica
03:31:37
Thanks so much Mauro (and the other experts)! Great presentation!
sintu rongpipi
03:31:50
how do we quantify texture from peak ratios?
Bikram
03:32:13
thanks for this talk
Gourab Bhaskar
03:32:37
Speardsheet would be helpful thanks
ssankara
03:32:59
Thank you very much for the informative presentation.
adam w
03:35:00
Thank you for a highly informative talk!
Tuhin Dey (TA)
03:36:05
In RSM how to choose asymmetric planes to determine 'In plane lattice constant' ?
Han-byul
03:37:45
It's about common problem I've faced when my material is not pure phase and having a number of secondary phases. In XRD peak identification, if I have one or two remained peaks and each of them is fitted to multiple phases in the program, how I can determine the phase and identify the residual peak? Any recommendation for accurate analysis?
Shiv Prakash Singh
03:38:40
Thanks! It was excellent talk!
Yang Wang
03:38:45
Great lecture! Thank you!
Han-byul
03:39:10
Thanks! Great lecture!
Gourab Bhaskar
03:39:15
Thank you so much appreciate it
Sikai
03:39:21
Thanks!
Qvas
03:39:22
Awesome presentation! Thank you so much!!
Shiv Prakash Singh
03:39:28
Its great idea to have a youtube chanell
Julio Soares
03:39:30
Great talk! Thanks Jeff, Thanks Mauro.
Md Abdul Halim
03:39:31
thanks a lot to organizers
Dmitri B
03:39:31
SAXS, please! Thank you Mauro and Jeff!